Clinical behavior of universal adhesives in non-carious cervical lesions: A randomized clinical trial.

OBJECTIVES: This randomized, double-blind clinical trial, , evaluated the behavior of two universal adhesives used in etch-and-rinse (ER) or self-etch (SE) approach in non-carious cervical lesions (NCCLs). METHODS: Two hundred and eleven NCCLs were selected in 54 participants and randomly allocated into four experimental groups: Scotchbond Universal Adhesive - SBU (3M Oral Care) and Prime & Bond Elect - PB (Dentsply Sirona) used in ER and SE modes. Two trained operators placed all resin composite restorations (Filtek Z250, 3M Oral Care). Restorations were evaluated at baseline and after 6 months using both FDI and USPHS modified criteria by a blinded calibrated examiner. Kruskal-Wallis and Mann-Whitney U non-parametric tests were used to compare the restoration failures among experimental groups. RESULTS: Statistically significant differences were found among groups regarding failures (p=0.000 for both FDI and USPHS criteria). PB-SE presented more failures (p<0.05) than other experimental groups. No significant difference was found between any other pair of groups (p>0.05). CONCLUSIONS: The etch and rinse approach affected the clinical performance of Prime and Bond Elect. For this material, the self-etch approach generated lower criteria scores after a six-month follow-up. The bonding strategy did not influence Scotchbond Universal Adhesive clinical performance. (RBR-2GQMVF) CLINICAL SIGNIFICANCE: The clinical behavior of mild universal adhesive Prime & Bond Elect depends on the bonding strategy. The etch-and-rinse approach is recommended for this adhesive system. Scotchbond Universal Adhesive can be used in both bonding strategies without impairing clinical performance.

Self-etch Approach of Universal Adhesives as an Alternative to Minimize Bond Degradation on Sound Dentin vs Caries-affected Dentin over Time.

PURPOSE: To investigate the influence of the etching strategy of universal adhesives on bond degradation to sound and artificially-induced caries-affected dentin. MATERIALS AND METHODS: The universal adhesives (Scotchbond Universal Adhesive; All-Bond Universal; Prime&Bond Elect) and adhesives used as controls (Adper Single Bond 2 and Clearfil SE Bond) were applied to sound and artificially-induced caries-affected bovine dentin. Microtensile bond strength was evaluated immediately (24 h) and after one year of water storage (1 year). Representative specimens were also prepared to assess nanoleakage. Bond strength data (MPa) were analyzed using three-way ANOVA and post-hoc Tukey's test (α = 0.05), considering each substrate separately. RESULTS: Bonding degradation was observed for all universal adhesives on caries-affected dentin, irrespective of the etching strategy. On sound dentin, bonding degradation was observed when adhesives were used on the etch-and-rinse strategy. CONCLUSION: The universal adhesives were not capable of maintaining bond stability over time on caries-affected dentin. The self-etch strategy seems better able to maintain the durability of adhesive interfaces created on sound dentin.

Phosphoric Acid Containing Chlorhexidine Compromises Bonding of Universal Adhesive.

PURPOSE: To examine the influence of phosphoric acid containing chlorhexidine on the dentin bond stability of a universal and a 2-step etch-and-rinse adhesive. MATERIALS AND METHODS: Eighty sound bovine incisors were randomly assigned to 8 groups (n = 10) according to: phosphoric acid (37% phosphoric acid [CTR] or 37% phosphoric acid with 2% chlorhexidine [CHX]); adhesive (Scotchbond Universal Adhesive [SBU]or Adper Single Bond 2 [SB2]); and water storage time (24 h and 6 months). Both acids and adhesives were applied to flat dentin surfaces (following manufacturer's instructions) upon which composite cylinders were built up (0.72 mm2). After storage in distilled water at 37°C for 24 h or 6 months, the composite cylinders were submitted to microshear bond strength (µSBS) testing. Bond strength data (MPa) were analyzed using three-way ANOVA and post-hoc Tukey's test (α = 5%). RESULTS: The interaction among factors was significant (p = 0.012). Both adhesives showed similar 24-h bond strengths regardless of the phosphoric acid. After 6 months, similar values were found for both materials when control phosphoric acid was used, but CHX phosphoric acid produced statistically significantly lower bond strengths for SBU. SB2 bond strength was not affected by acid type. CONCLUSION: Phosphoric acid containing chlorhexidine induced premature bond strength degradation of Scotchbond Universal Adhesive.

Internal adjustments decrease the fatigue failure load of bonded simplified lithium disilicate restorations.

OBJECTIVE: To investigate the effect of intaglio surface adjustment of simplified lithium disilicate ceramic restorations adhesively cemented to a dentin-like material on its fatigue behavior. METHODS: Ceramic discs (IPS e.max CAD) were prepared and an in-Lab simulation of machining roughness was performed by grinding with SiC paper (#60). Ceramic discs were divided into 4 groups according to the internal adjustment of the cementation surface: no adjustments (CTRL); adjustment with a medium (M), fine (F), or extra fine (FF) diamond bur. Dentin-like material discs were also produced. Ceramic disc intaglio surfaces were etched (5% hydrofluoric acid; 20s) and received a silane coating. Dentin-like material discs were etched (10% hydrofluoric acid; 1min) and received a primer coating. Pairs of ceramic/dentin-like material were adhesively cemented (Multilink Automix), and fatigue failure load tests were performed using the Staircase approach (250,000 cycles; 20Hz). Roughness, topographic and fractographic analyses were performed. Statistical analyses were carried out through ANOVA tests. RESULTS: All ground groups (M=521.3 N; F=536.9 N; FF=676.2 N) presented lower fatigue failure load values than the control (1241.6 N). M diamond bur created a rougher surface than F (Ra and Rz parameters). However, FF was similar to F and M for Ra, and similar to F for Rz. SIGNIFICANCE: Bur adjustments on the intaglio surface of simplified lithium disilicate ceramic restorations greatly decreased the fatigue failure load even using an extra-fine diamond bur. Care should be taken when internal adjustments are needed.

The impact of artificially caries-affected dentin on bond strength of multi-mode adhesives.

AIM: The aim of this study is to evaluate the impact of dentin condition on bond strength of multi-mode adhesive systems (MMAS) to sound and artificially induced caries-affected dentin (CAD). METHODS: Flat dentin surfaces of 112 bovine incisors were assigned to 16 subgroups (n = 7) according to the substrate condition (sound and CAD- pH-cycling for 14 days); adhesive systems (Scotchbond Universal, All-Bond Universal, Prime and Bond Elect, Adper Single Bond Plus and Clearfil SE Bond) and etching strategy (etch-and-rinse and self-etch). All systems were applied according to the manufacturer's instructions, and resin composite restorations were built. After 24 h of water storage, specimens were sectioned (0.8 mm2) and submitted to the microtensile test. STATISTICAL ANALYSIS: Data (MPa) were analyzed using three-way analysis of variance and Tukey's test (α = 0.05). RESULTS: MMAS presented similar bond strength values, regardless etching strategy in each substrate condition. Bond strength values were lower when MMAS were applied to CAD in the etch-and-rinse strategy. CONCLUSION: The etching strategy did not influence the bond strength of MMAS to sound or CAD, considering each substrate separately. However, CAD impact negatively on bond strength of MMAS in etch-and rinse mode.